What is surface treatment?

Surface energy of solid materials and the need for surface treatment of polymers. It is often necessary to bond plastic materials to metals or other plastic materials, or simply print on a plastic surface. In order to successfully accomplish this the liquid adhesive, or ink should be able to wet the surface of the material. And this is where Corona Treatment and Plasma Treatment technologies are necessary.

Wettability depends on one specific property of the surface: Surface energy, often referred to as surface tension. Surface energy, like surface tension is measured in mN/m. The surface energy of the solid substrate directly affects how well a liquid wets the surface. The wettability, in turn, is easily demonstrated by contact angle measurements. The contact angle is the angle between the tangent line at the contact point and the horizontal line of the solid surface. When a liquid droplet is set on a smooth solid horizontal surface, it may spread out over substrate and the contact angle will approach zero if complete wetting takes place. Conversely, if wetting is partial, the resulting contact angle reaches equilibrium in the range 0 to 180 degrees.

Surface Wettability

surface wettabilityFig 1 to your left helps illustrate the difference between good and poor wettability. The higher the surface energy of the solid substrate in relation to the surface tension of the liquid, the better its wettability, and the smaller the contact angle. In order for a proper bond to exist between a liquid and a substrate surface, the substrate’s surface energy should exceed the liquid’s tension by about 2-10 mN/m.

surface energy solid materialsFig. 2: Surface Energy Solid Materials
Fig 2 to your right shows absolute values of surface energy for solid materials and the surface tension of many plastics including polyethylene and polypropylene is often insufficient for bonding or printing.

These materials have very useful properties such as chemical inertness, a low coefficient of friction, high wear, puncture and tear resistance, etc.

However, the poor wettability of these polymers presents the designer with the problem of bonding or decorating these materials. Surface treatment can improve wettability of the material by raising the material’s surface energy and positively affect adhesive characteristics by creating bonding sites. The most advanced and successful methods of surface treatment are based on a principle of high voltage discharge in air.

Basics of high voltage discharge in air and its application to surface treatment

In the presence of a high voltage discharge in an air gap, free electrons, which are always present in the air, accelerate and ionise the gas. When the electric discharge is very strong, collisions of high velocity electrons with molecules of gas result in no loss in momentum, and electron avalanching occurs. When a plastic part is placed in the discharge path, the electrons generated in the discharge impact the surface with energies 2 to 3 times that necessary to break the molecular bonds on the surface of most substrates. This creates very reactive free radicals. These free radicals in the presence of oxygen can react rapidly to form various chemical functiona groups on the substrate surface. Functional groups resulting from this oxidation reaction are the most effective at increasing surface energy and enhancing chemical bonding to the resin matrix. These include carbonyl (-C=O-). carboxyl (HOOC-), hydroperoxide (HOO-) and hydroxyl (HO-) groups.

Surface treatment with high voltage discharge modifies only the surface characteristics without affecting material bulk properties.

est technologyTantec three-dimensional electrical surface treatment (EST) technology is based on the high voltage high frequency discharge in air. Three-dimensional objects are passed through a discharge region between two electrodes (Figure 3 to your left).

The discharge is sustained in a large gap between the electrodes by establishing a high potential difference between the electrodes. High applied voltage is only one condition for effective treatment. An uniform treatment of parts moving at high speed requires high efficiency energy transfer from the power source to the discharge region. Corona discharge at frequencies of 15-25 kHz accomplishes high efficiency energy transfer as electrons oscillate in the gap between the electrodes. It has been shown that the higher the frequency the lower the power to achieve a given treatment level.

The EST technology achieves a uniform treatment of surfaces of three-dimensional objects on high-speed lines through maintaining a potential difference between electrodes up to 80 kV at frequencies between 15-25 kHz. Under these conditions objects with cross-sections as large as 4 inches (100 mm) can be treated on-line as they continually move through a treating chamber.
An Electrical Surface Treatment system consists of high frequency generator, high voltage transformer and treating electrodes. The generator produces an output signal whose frequency is automatically adjusted in the 15-25 kHz range depending on the load impedance, thus optimising the power available for treatment. The high voltage transformer steps up the output signal from the generator to the level needed to generate the discharge of desired intensity. The treating station is designed around two electrodes: a treating electrode and counter electrode (usually at a ground potential). The electrodes are engineered for each application.

Tantec offers a selection of Plasma treaters for plasma surface treatment of different materials. See our list of products at our plasma products page: Plasma treatment equipment

Applications of Tantec Electrical Surface Treatment Technology ( EST)

The following materials have been successfully treated using EST technology:

  • Polyethylene (PE) * Plexiglas (PMMA)
  • Polypropylene (PP) * Teflon (PTFE)
  • Polystyrene (PS) * Polycarbonat (PC)
  • EPDM-rubber * Polyurethane (PUR)
  • ABS etc.

Here are some specific applications:

  • Treatment of surfaces of bio-medical testing devices to improve wettability of surfaces for confluent liquid flow.
  • Treatment of syringe barrels prior to printing.
  • Treatment of the inner surface of needle hubs prior to bonding a stainless steel needle.
  • Treatment of electronic cable insulation to improve adhesion of inks and coatings.
  • Treatment of lids and covers of chemical containers prior to gasket material application or printing.
  • Treatment of plastic bottles prior to application of adhesive labels.
  • Treatment of automotive profiles made of EPDM rubber prior to application of an adhesive for retaining flocking bristles or decorating fabric.

Shelf life of treated surfaces

The shelf life of pre-treated materials ranges from hours to years, depending on the plastic, its formulation, how it was treated and its exposure to elevated temperature after treatment. Material purity is the most important factor. Shelf life is limited by the presence of low molecular weight components such as antiblock agents, mould release, antistatics, etc. Eventually, these components migrate to the surface of clean polymers. It is therefore recommended to print or bond to the material soon after treatment. However, once the treated surface has been interfaced with a coating, ink, adhesive, or another material, the bond becomes permanent.


  • Tantec surface treaters are sold worldwide to end-users and OEM’s through our own branch offices and more than 30 partners worldwide.

  • Leading manufacturer of standard and customized Plasma and Corona systems for surface treatment of plastics and metals to enhance adhesion properties.

  • The Tantec Group is an innovative organization with a high level of know-how, continuously developing new Plasma and Corona equipment to help solving adhesion problems, and to meet high customer demands.

We use cookies to improve our website and your experience when using it. Cookies used for the essential operation of the site have already been set. To find out more about the cookies we use and how to delete them, see our Privacy Policy.

I accept cookies from this site